Product Details:
Payment & Shipping Terms:
|
| Classification: | Heating Element | Application: | High Temperature Furnace |
|---|---|---|---|
| Shape: | Straight/U/W/UL | Material: | MoSi2 |
| Installation: | Vertical Installation | Diameter: | 3/6mm, 4/8mm |
| Hot Zone Length: | 100-1500mm | Surface Load: | 10/14.5W/cm2 |
| High Light: | MoSi2 high temperature heating element,furnace MoSi2 heating element |
||
What’s theMosi2 Electric Heater Element?
Molybdenum disilicide(MoSi2) heating element is one resistance heating component made from MoSi2 or as the basic material. When it’s heated to high temperature under the oxidizing atmosphere, one dense MoSi2film will be formed on its surface to protect the element against oxidizing further. Therefore, the element has unique anti-oxidation property under high temperature atmosphere. The highest temperature can reach 1800°C, the applicable temperature is between 500-1700°C.
Precaution for use:
1. The heating element of silicon molybdenum rod should not be used in the temperature range of 400 ℃ to 700 ℃, so under this unfavorable condition, the component will undergo low temperature oxidation and damage the component.
2. The heating element of silicon molybdenum rod is suitable for use in air and neutral atmosphere. The reducing atmosphere such as hydrogen will destroy the protective layer, and the steam of chlorine and sulfur will directly damage the element.
3. Silicon molybdenum rods are somewhat softened at high temperatures (above 1500 degrees), and they are hard and brittle at low temperatures. In order to avoid stress during temperature changes, which is conducive to thermal expansion and contraction of components, it is best to use a free vertical hanging installation method . The disassembly and replacement of the hoisting components is more convenient. It is not necessary to wait for the furnace to cool down, and it can be replaced in a hot state.
Application of MoSi2 heater:
| Item | name | distinction criterion | specification | Using range |
| Heating elements | 1700 type | Element operating temperature 1700℃ is acceptable |
Le Φ 6-12W type/U type/L type/all kinds of hetero type / stripe shape |
high temperature electric resistance furnace |
| 1800 type | Element operating temperature 1800℃ is acceptable | |||
| 1800J type | Element operating temperature≥1800℃ |
Le Φ 3-12W type |
Special,high temperature and high-power electric resistance furnace | |
| 1800T type | Element operating temperature≤1800℃ |
Le Φ 3-12W type U type |
Not oxidized special air high temperature electric resistance furnace |
Physcial property of molybdenum disilicide heating element MoSi2 rod:
| Density | Bending Strength | Hardness | Apparent Porosity | Water Absorption | Elongation | Fracture Toughness | Compressive Strength |
| 5.8g/cm3 | 350Mpa | 12.0Gpa | ±2% | 0 | 4% | 4.5Mpa.m1/2 | 650Mpa |
Packaging & Shipping
1. From the inside to outer packaging, is foam sponge, carton, wooden case.
2. Sea or Air transportation, DHL express.
3. Please make sure the 'shipping address' is your confirmed address.
4. We do check everything in good condition before we ship your parcel out.
5. We will process your order ASAP after payment is confirmed.
Please tell us the following data of molybdenum disilicide MoSi2 rod heating element when send enquiry to us :
d = the diameter of hot zone ?
c = the diameter of cold zone ?
Le = the length of hot zone ?
Lu = the length of cold zone ?
a=Shank spacing
g=junction length
How many pcs ?